http://cio.repositorioinstitucional.mx/jspui/handle/1002/907| Synthesis of Lu2O3:Eu3+ Luminescent Ceramic Powder Embedded in SiO2 Matrix | |
| Haggeo Desirena Enrriquez Elder de la Rosa Cruz | |
| En Embargo | |
| 26-11-2019 | |
| Atribución-NoComercial-SinDerivadas | |
| In the present work, the effect of SiO2 was analyzed in different molar ratios (Lu : Si = 4 : 1, 6 : 1, 8 : 1, 10 : 1 and 1 : 0), in order to prepare SiO2 embedded Lu2O3:Eu3+ sol-gel luminescent powders, from a modified PVP-containing solution. The crystalized SiO2 embedded Lu2O3:Eu3+ powders were characterized by Fourier transform infrared spectroscopy revealing the presence of high intensity bands associated with siloxanes groups at 700°C, which could indicate a cross-linked Si-O groups to Lu2O3:Eu3+. X-ray diffraction results showed that cubic phase was present in the powder heat treated at 500°C and remained up to 700°C. The powders SiO2 embedded Lu2O3:Eu3+ powders in molar ratio Lu:Si 4 : 1 and 10 : 1 masked the crystallinity of glass ceramic. The SiO2 effect on the morphology of the glass ceramic systems was monitored by scanning electron microscopy observations, from these results homogenous particles were obtained for Lu:Si 6 : 1 and 8 : 1 systems. Photoluminescence studies showed that adding silica to the ceramic systems increases the typical emission to around λem = 611 nm. | |
| 25-11-2014 | |
| Artículo | |
| CIENCIAS FÍSICO MATEMÁTICAS Y CIENCIAS DE LA TIERRA | |
| Aparece en las colecciones: | Articulos Arbitrados 2014 |